Resistive random access memory cells having doped current limiting layers

ABSTRACT

Provided are semiconductor devices, such as resistive random access memory (ReRAM) cells, that include current limiting layers formed from doped metal oxides and/or nitrides. These current limiting layers may have resistivities of at least about 1 Ohm-cm. This resistivity level is maintained even when the layers are subjected to strong electrical fields and/or high temperature annealing. In some embodiments, the breakdown voltage of a current limiting layer may be at least about 8V. Some examples of such current limiting layers include titanium oxide doped with niobium, tin oxide doped with antimony, and zinc oxide doped with aluminum. Dopants and base materials may be deposited as separate sub-layers and then redistributed by annealing or may be co-deposited using reactive sputtering or co-sputtering. The high resistivity of the layers allows scaling down the size of the semiconductor devices including these layer while maintaining their performance.

TECHNICAL FIELD

The present invention relates generally to semiconductor devices and more specifically to resistive random access memory (ReRAM) cells having doped current limiting layers.

BACKGROUND

Nonvolatile memory is computer memory capable of retaining the stored information even when unpowered. Non-volatile memory is typically used for the task of secondary storage or long-term persistent storage and may be used in addition to volatile memory, which losses the stored information when unpowered. Nonvolatile memory can be permanently integrated into computer systems (e.g., solid state hard drives) or can take the form of removable and easily transportable memory cards (e.g., USB flash drives). Nonvolatile memory is becoming more popular because of its small size/high density, low power consumption, fast read and write rates, retention, and other characteristics.

Flash memory is a common type of nonvolatile memory because of its high density and low fabrication costs. Flash memory is a transistor-based memory device that uses multiple gates per transistor and quantum tunneling for storing the information on its memory device. Flash memory uses a block-access architecture that can result in long access, erase, and write times. Flash memory also suffers from low endurance, high power consumption, and scaling limitations.

The constantly increasing speed of electronic devices and storage demand drive new requirements for nonvolatile memory. For example, nonvolatile memory is expected to replace hard drives in some computer systems. However, transistor-based flash memory is often inadequate to meet the requirements of various applications. New types of memory, such as resistive random access memory (ReRAM), are being developed to meet these demands and requirements.

SUMMARY

Provided are semiconductor devices, such as resistive random access memory (ReRAM) cells, that include current limiting layers formed from doped metal oxides and/or nitrides. These current limiting layers may have resistivities of at least about 1 Ohm-cm. This resistivity level is maintained even when the layers are subjected to strong electrical fields and/or high temperature processing. In some embodiments, the breakdown voltage of a current limiting layer is at least about 8V. Some examples of materials for such current limiting layers include titanium oxide doped with niobium, tin oxide doped with antimony, and zinc oxide doped with aluminum. Dopants and base materials may be deposited as separate sub-layers and then redistributed by annealing or may be co-deposited using reactive sputtering or co-sputtering. The high resistivity of the layers allows scaling the down the size of the semiconductor devices including these layer while maintaining their performance.

In some embodiments, a resistive random access memory cell includes a first electrode layer, a second electrode layer, a third layer operable as a current limiter, and a fourth layer operable as a resistive switching layer. The third layer may include a metal oxide and a dopant. It may have a breakdown voltage of at least 8V and a resistivity of at least 1 Ohm-cm. The third layer may be disposed between the first electrode layer and the second electrode layer. The fourth layer may include a resistive switching material and be disposed between the first electrode layer and the second electrode layer.

In some embodiments, the third layer includes titanium oxide doped with niobium. The third layer may include tin oxide doped with antimony. In some embodiments, the third layer includes zinc oxide doped with aluminum. The dopant concentration in the third layer may be between about 0.5 atomic percent and 25 atomic percent or, more specifically, between about 1 atomic percent and 10 atomic percent. In some embodiments, the third layer has a resistivity of at least 1 Ohm-cm or, more specifically, at least about 1 Ohm-cm. The resistivity of the third layer may change by less than 10% upon applying an electrical field of 1 MV/cm. The third layer may have a thickness of less than about 200 Angstroms or, more specifically, less than about 100 Angstroms and even less than about 50 Angstroms. In some embodiments, the third layer has an amorphous structure.

The resistive switching material may include one of hafnium oxide, aluminum oxide, tantalum oxide, zirconium oxide, or yttrium oxide. The first electrode layer may include one of silicon, titanium, titanium nitride, platinum, iridium, iridium oxide, ruthenium, or ruthenium oxide. In some embodiments, the resistive random access memory cell also includes a barrier layer disposed between the third layer and the fourth layer.

In some embodiments, a resistive random access memory cell includes a first electrode layer including n-doped polysilicon and a second electrode layer including titanium nitride. The resistive random access memory cell also includes a third layer operable as a current limiter. The third layer includes titanium oxide doped with niobium such that the concentration of niobium in titanium oxide is between about 1 atomic percent and 10 atomic percent. The third layer has a breakdown voltage of at least about 8V and a resistivity of at least about 1 Ohm-cm. The third layer is disposed between the first electrode layer and the second electrode layer and has a thickness of less than about 100 Angstroms. The resistive random access memory cell also includes a fourth layer operable as a resistive switching layer and including hafnium oxide. The fourth layer is disposed between the first electrode layer and the second electrode layer.

Provided also is a method of forming a resistive random access memory cell. The method may involve forming a first electrode layer over a substrate and forming a third layer on the first electrode layer. The third layer is operable as a current limiter and includes a metal oxide and a dopant. The third layer may have a breakdown voltage of at least about 8V and a resistivity of at least about 1 Ohm-cm. The method may involve forming a fourth layer on the third layer and then forming a second electrode layer on the fourth layer. The fourth layer is operable as a resistive switching layer and includes a resistive switching material. The third layer may be formed using one of a reactive sputtering technique, a co-sputtering technique, or an atomic layer deposition technique. In some embodiments, forming the third layer may involve transferring the dopant from the fourth layer and into the third layer by annealing.

BRIEF DESCRIPTION OF THE DRAWINGS

So that the manner in which the above recited features of the present invention can be understood in detail, a more particular description of the invention, briefly summarized above, may be had by reference to embodiments, some of which are illustrated in the appended drawings. It is to be noted, however, that the appended drawings illustrate only typical embodiments of this invention and are therefore not to be considered limiting of its scope, for the invention may admit to other equally effective embodiments.

FIG. 1 illustrates a schematic representation of an array including multiple ReRAM cells, in accordance with some embodiments.

FIG. 2 is a graph illustrating the current versus voltage characteristics of the high and low resistance I-V curves of a resistive switching layer, in accordance with some embodiments.

FIG. 3 is a current versus time plot illustrating the effect of delivering bipolar type switching pulses through a memory element, in accordance with some embodiments.

FIG. 4 is a schematic side cross-sectional view of a ReRAM cell, in accordance with some embodiments.

FIG. 5 is a schematic representation of an electrical circuit corresponding to the ReRAM cell illustrated in FIG. 4, in accordance with some embodiments.

FIG. 6 is a graph illustrating power loss versus the magnitude of the current limiting layer resistance when a switching or sensing current is delivered through the current limiting layer, in accordance with some embodiments.

FIG. 7 is a process flowchart corresponding to a method of forming a ReRAM cell, in accordance with some embodiments.

While the foregoing is directed to embodiments of the present invention, other and further embodiments of the invention may be devised without departing from the basic scope thereof, and the scope thereof is determined by the claims that follow.

DETAILED DESCRIPTION Introduction

A ReRAM cell exhibiting resistive switching characteristics generally includes multiple layers formed into a stack. This stack is often referred to as a Metal-Insulator-Metal (MIM) stack. The stack includes two conductive layers operating as electrodes, which may include metals and other conductive materials, such as doped silicon. These conductive layers are identified as “M” in the above naming convention. The stack also includes a resistive switching layer, which is made from less conductive materials than the electrodes. As such, this layer is labeled as “I” for an insulator. This layer exhibits resistive switching properties characterized by different resistive states, which may be used to store one or more bits of information. For example, one resistive state may be used to represent a logical “zero,” while another resistive state may be used to represent a logical “one.” The difference in the resistive states may be attributed to changes in the insulator layer, changes at one or both interfaces between the insulator layer and metal layers, or both types of changes. The stack may also include other layers as further described above, such as a current limiting layer, a current steering layer, a barrier layer, and the like.

A current limiting layer may be provided in a ReRAM cell to limit the current through the cell and prevent unintentional damage to various layers of the cell. As a result, performance and life time of the ReRAM cell may be improved. Embedding the current limiting layer into the cell such that the current limiting layer directly interfaces the resistive switching layer or being positioned close to the resistive switching layer may be important, particularly in ReRAM cells that utilize high speed programming pulses as further explained below. The current limiting layer may be formed from a material that does not significantly vary in resistivity when the “set” and “reset” voltages are applied to the cell contrary to the resistive switching layer. This resistance stability assures that switching characteristics of the cell will not change over its lifetime.

Provided are semiconductor devices, such as resistive random access memory (ReRAM) cells, that include current limiting layers formed from doped metal oxides and/or nitrides. Some examples of such current limiting layers include titanium oxide doped with niobium, tin oxide doped with antimony, and zinc oxide doped with aluminum. The dopant concentration in the current limiting layer can vary between 0.5 and 25 atomic %. Adding dopants into the current limiting layer provides new materials options that have not been previously available. For example, dopant concentrations can be precisely controlled to achieve desirable resistivities of the current limiting layers. Furthermore, new types of materials are used. These current limiting layers may be coupled with resistive switching layers formed from hafnium oxide, aluminum oxide, zirconium oxide, and other resistive switching materials. The high resistivity of the layers allows scaling down the size of the semiconductor devices including these layers while maintaining their performance.

In some embodiments, a current limiting layer has a resistivity of at least about 1 Ohm-cm or, more specifically, at least about 10 Ohm-cm. This resistivity level is maintained even when the layers are subjected to strong electrical fields and/or high temperature annealing. In some embodiments, the breakdown voltage of a current limiting layer may be at least about 8V. Dopants and base materials may be deposited as separate sub-layers and then redistributed by annealing or may be co-deposited using reactive sputtering or co-sputtering.

Examples of Re-RAM Cells

FIG. 1 illustrates a schematic representation of a memory array 100 including multiple ReRAM cells 106, in accordance with some embodiments. Memory array 100 may be a part of a larger memory device or other integrated circuit structure, such as a system on a chip type device. ReRAM cells 106 are connected to their control circuitry (e.g., read and write circuitry) by word lines and bit lines, which are illustrated as electrode layers 102 and 104 in FIG. 1. The word lines and bit lines may be orthogonal to form a cross-type array. Each word and bit line may be shared by multiple ReRAM cells. In some embodiments (further described below), only portions of electrode layers 102 and 104 (i.e., sub-layers) form corresponding word lines and bit lines, while the remaining portions of these layers are constrained within the boundaries of each cell.

Electrode layers 102 and 104 are used to read from or write data into ReRAM cells 106. Multiple ReRAM cells may share one electrode, but each ReRAM cell includes a unique combination of two electrodes. That is, no two ReRAM cells in array 100 share the same two electrodes. In addition to communication functions, electrode layers 102 and 104 may be used to provide resistive switching characteristics with ReRAM cells.

Electrode layers 102 and 104 include one or more conductive sub-layers. In a multilayered electrode, each layer may have a designated function and is made from specific material. For example, electrode layers 102 and 104 may each include two or more conductive sub-layers. One of these sub-layers may be used to interconnect multiple ReRAM cells 200 in the array (i.e., perform function of bit and word line), while another sub-layer may provide a desirable electrical interface (e.g., desirable work function) to a resistive switching layer. In this example, one sub-layer of the electrode layer is shared by multiple ReRAM cells, while another sub-layer is specific to each ReRAM cell.

Operation of ReRAM cells will now be described with reference to FIGS. 2 and 3. The resistive state of a ReRAM cell can be sensed by applying a sensing voltage (i.e., a “read” voltage V_(READ) shown in FIG. 2) to its electrode layers or, more specifically, to a specific combination of a word and bit lines. In some embodiments, the read voltage may be about +0.5 volts (V). Depending on its history, a memory element that is addressed in this way may be in either a high resistance state (HRS) or a low resistance state (LRS). The resistance of the ReRAM cell therefore determines what digital data is being stored by the ReRAM cell. For example, of the ReRAM cell is in the HRS, for example, the memory element may be said to contain a logic “zero” (i.e., a “0” bit). If, on the other hand, the memory element is in the LRS, the memory element may be said to contain a logic “one” (i.e., a “1” bit). Of course, an opposite data assignment scheme may be used as well. That is, the HRS may correspond to the logic “one” while the LRS may correspond to the logic “zero.” During a write operation, the state of a ReRAM cell can be changed by applying a suitable write signals to its electrode layers.

In some embodiments, a ReRAM cell uses bipolar switching where opposite polarity “set” and “reset” voltages are used to alter the resistance of the memory element between its HRS and LRS. FIG. 2 schematically illustrates a log-log plot of current (I) versus voltage (V) of one example of the LRS and HRS curves of a ReRAM cell having these two bistable resistive states. The voltage levels V_(SET) and V_(RESET), shown in FIG. 2, illustrate typical threshold values used to “set” and “reset” the contents of the ReRAM cell.

At some point, the ReRAM cell may be in its HRS, which can be sensed by the read and write circuitry using cell's electrode layers. Specifically, the read and write circuitry may apply a read voltage V_(READ) to the ReRAM cell and can sense the resulting “off” current (I_(OFF)) that flows through the cell. When it is desired to switch from one logic state into another to store a different value, the cell can be placed into its LRS. This may be accomplished by using the read and write circuitry to apply a “set” voltage V_(SET) (e.g., −1 V to −4 V) across the cell's electrode layers. In some embodiments, applying a negative V_(SET) voltage to the ReRAM cell causes the cell to switch to its LRS. It is believed that the change in the resistive state of the ReRAM cell may be due to the redistribution or filling of traps (i.e., “trap-mediated”), or defects, in the resistive switching layer when the device is reverse biased. The resistive switching layer, which is disposed in the ReRAM cell, will generally have at least two bistable resistive states, i.e., LRS and HRS. It is believed that the defects or traps, which are commonly formed during the deposition or initial burn-in or forming of the resistive switching layer, are often created by a non-stoichiometric material composition found in the formed resistive switching layer. V_(SET) and V_(RESET) are generally referred to as “switching voltages” herein.

The LRS of the ReRAM cell can be sensed using the read and write circuitry. When a read voltage V_(READ) is applied to resistive switching ReRAM cell, the read and write circuitry will sense the relatively high “on” current value (I_(ON)), indicating that ReRAM cell is in its LRS. When it is desired to change the logic state, the resistive switching layer can once again be placed in its HRS by applying a positive “reset” voltage V_(RESET) (e.g., +1 V to +5 V) to cell. When the “reset” voltage V_(RESET) is removed from the cell, the cell can once again be characterized by its high resistance when the read voltage V_(READ) is applied. Voltage pulses can be used in the programming of the ReRAM cell. For example, a 1 microseconds to 1 nanoseconds square or trapezoidal shaped pulse can be used to switch the cell. In some embodiments, it may be desirable to adjust the length of the pulse depending on the amount of time needed to switch the cell. In one example, the “set” and “reset” pulses are each about 10 ns in length. While the discussion of the ReRAM cell herein primarily provides bipolar switching examples, some embodiments of the ReRAM cell may use unipolar switching, where the “set” and “reset” voltages have the same polarity, without deviating from the scope of the invention described herein.

To provide a measurable difference between the logic “zero” and logic “one” states, it is common to form the resistive switching layer such that the I_(ON) and I_(OFF) currents have a difference of at least five times (e.g., current ratio I_(ON)/I_(OFF)≧5). In some examples, the difference between the logic “zero” and logic “one” states is at least one order of magnitude (e.g., current ratio I_(ON)/I_(OFF)≧10). In other words, the ratio of the electrical resistances of the resistive switching layer is decreased by at least a factor of 5 to 10 when switching from the high to the low resistance state.

Fabrication of a ReRAM cell may involve applying a forming voltage V_(FORM) at least once through the cell in order to “burn-in” the cell. It is believed that the application of a forming voltage, which is typically significantly greater than the reset V_(RESET) and set V_(SET) voltages, causes formation and/or redistribution of the defects within the resistive switching layer. Specifically, the defects can move, align and/or collect within various regions of the resistive switching layer, causing the resistive switching layer to consistently and reliably switch between the LRS and HRS throughout the memory element's life. In some embodiments, the forming voltage V_(FORM) is between about 1 and about 5 times greater than the reset V_(RESET) or set V_(SET) voltage. Specifically, the forming voltage V_(FORM) may be between about 1.4 and about 2.5 times greater than the reset V_(RESET) or set V_(SET) voltage. In some embodiments, the forming voltage V_(FORM) is between about 3 and about 7 volts. In some embodiments, a ReRAM cell may be fabricated in such a way that the application of a forming voltage is not required at all to assure that the cell performs as desired throughout its life.

FIG. 3 is a plot of current versus time for a plurality of bipolar type “set” and “reset” switching pulses, as illustrated by pulses 201-206, that are delivered to a ReRAM cell in accordance with some embodiments. In one example, as shown in FIG. 3, a cell programming step may include the delivery of a “set” switching pulse 211, a “reset” switching pulse 213, and two “sensing” pulses 212. To assure that the ReRAM cell reliably switches from its HRS to its LRS and vice versa, one must assure that the “set” switching pulse 211 produces a current that is greater than a minimum “set” current I_(MSC), which is defined as the minimum current required to flow through the resistive switching layer to cause it to switch from a high resistance state (e.g., 2.5 MΩ) to a low resistance state (e.g., <<250 kΩ). In some embodiments, the HRS and LRS of a resistive switching layer may be about 2.5 MΩ and about 100 kΩ, respectively.

Similarly, to assure that the ReRAM cell reliably switches from its LRS to its HRS the “reset” switching pulse 213 will generally be delivered at a current level that is greater than a minimum “reset” current I_(MRC), which is defined as the minimum current required to flow through the resistive switching layer to cause it to switch from a low resistance state to a high resistance state. It should be noted that the minimum “set” current I_(MSC) and minimum “reset” current I_(MRC) are related to the physical and/or electrical properties of the material in resistive switching layer 404, and thus may be adjusted by careful selection of the material(s) and/or physical properties (e.g., thickness) of the resistive switching layer and by performing various post-processing steps on the formed layer. In some examples, by controlling the number of defects in the formed the resistive switching layer, such as by adjusting the stoichiometry of the material(s) found in the resistive switching layer (e.g., HfO_(1.7) vs. HfO₂) during the layer formation process, the minimum switching currents can be adjusted.

Referring to FIGS. 2 and 3, in some examples, when a “set” switching pulse 211 is delivered to the ReRAM cell, the cell switches from its HRS to its LRS as shown by arrow 221. One will note that the current flowing through the ReRAM cell will shift from the initial “set” current I_(A) to the final “set” current I_(B) during the “set” operation, due to the change in resistance of the resistive switching layer. One will note that the initial “set” current I_(A) will typically equal the minimum “set” current I_(MSC), which was discussed above.

Alternately, when a “reset” switching pulse 213 is delivered to the ReRAM cell, the cell switches from its LRS to its HRS as shown by the arrow 222. One will note that the current flowing through the ReRAM cell will shift from the initial “reset” current I_(C) to the final “reset” current I_(D) during the “reset” operation, due to the change in resistance of the resistive switching layer.

Referring to FIG. 3, in some examples, a “set” switching pulse 211 is delivered to the ReRAM cell to create a LRS (e.g., or logic “one” state). In this case, a “set” voltage V_(SET) is applied across the electrode layers, which creates a first “set” current I₁ to flow through the cell, due to the impedance of the electrical components found in the cell. The first “set” current I₁ is equal to the applied “set” voltage V_(SET) divided by the sum of the impedances of the cell.

It is understood that the most damage to the components of the ReRAM cell occurs when a large current is delivered through the cell. Pulse 211 schematically illustrated in FIG. 3 focuses on the later stages of the “set” operation. The first “set” current I₁ achieved during the later stages of the “set” switching pulse 411 will generally equal the final “set” current I_(B). In general, the first “set” current I₁ will vary during the time that the “set” pulse 411 is applied to the cell. The first “set” current I₁ may have low current region 209 that is created due to the electrical properties of the material as it switches from the HRS to the LRS. The “set” pulse 411 may also have the final “set” current region as discussed above.

The resistance of the electrode layers is generally small to reduce power generation within the cell and/or array. The resistance of the resistance switching layer is desirably low at the end of the “set” operation (e.g., I₁=I_(B)), i.e., when the layer is its LRS. When a current steering element (e.g., a diode) is provided in the cell, its resistance will dominate in the cell. In other words, the resistance of the cell is approximately equal to the resistance of the current steering element. As such, the magnitude of the “set” current I₁ created by the switching pulse 201 may be equal the maximum current, or load current I_(L) (FIG. 3), which is approximately equal to the “set” voltage divided by the impedance of the current steering element. One will note that the difference between the “set” current I₁ and the minimum I_(MSC) current is much larger than necessary to cause the device to reliably switch to the logic “one” state. However, in practice it has been found that the high currents delivered through the cell can permanently damage the memory element components and cause cross-talk to occur between adjacently connected devices. One will note that the magnitude of the “set” current is particularly important for bipolar switching applications that require the current steering element to be reverse biased to “set” the resistance of the memory element into a low resistance state. In this case, the act of driving a high current through the current steering element, in a non-forward direction, can breakdown, generate heat within and ultimately damage the current steering element.

It has been found that, if the current steering element provides the primary voltage drop in the cell during the “set” operation as described above, the current steering element often is required to operate near its breakdown voltage to reliably cause the resistive switching layer to switch. Eventually, the current steering element may damage (i.e., breakdown), which will cause its impedance to drop. For example, the resistance of an undamaged reverse biased diode type current steering element may be in a range of about 1 and 100 mega-ohms, while the resistance of a forward biased diode type current steering element may be between about 1 and about 20 kilo-ohms.

Therefore, after performing the “set” operation by applying the “set” switching pulse 211, it is common to apply a “sensing” pulse 212 to assure that the logic “one” state has been achieved and the cell is still not damaged. The application of sensing pulse 212 is generally performed by applying a V_(READ) voltage across the cell. If the “set” operation was performed correctly, the current through the cell during this sensing operation will be equal to the I_(ON) current (which is equal to the V_(READ) voltage divided by the impedance of the cell). For a cell that has a resistive switching layer in its LRS, the I_(ON) current will approximately be equal to the V_(READ) voltage divided by the impedance of the current steering element.

Next, in cases where it desirable to change the ReRAM cell from a low resistance state (i.e., logic “one” state) to a high resistance state (i.e., logic “zero” state) a “reset” switching pulse 213, such as “reset” switching pulse 205, is delivered to the ReRAM cell. One will note that the largest current that is delivered through the ReRAM cell during the “reset” operation will be achieved when the initial “reset” current I_(C) flows through the device. The current flowing through the device during the “reset” operation will then tend to drop as the resistive switching layer 204 switches from its LRS to its HRS. Therefore, pulse 213, which is schematically illustrated in FIG. 3, may have a high current portion 219 at the start of the delivered pulse 213 and a stable region that equals the “reset” current I₄ during the later stages of the “reset” operation. Therefore, the “reset” current I₄ achieved during for most of duration of the “reset” switching pulse 213 will equal the final “reset” current I_(D) and the maximum current achieved during the pulse 413 will equal the initial “reset” current I_(C). It has been found that the magnitude of the current required to switch the ReRAM cell to its HRS from its LRS depends on the magnitude of the current used to “set” the cell in its LRS. If a high “set” current, such as current I₁, is delivered to the ReRAM cell, then a higher “reset” current is required to achieve a desirable high resistance state. Stated another way, the difference between the initial “reset” current I_(C), and/or the final “reset” current I_(D), and the minimum “reset” current I_(MRC) current needs to be larger than necessary to cause the device to switch from the “on” to the “off” state if the magnitude of the prior applied “set” current is too far from the minimum “set” current I_(MSC). The larger than necessary swings in the current used to switch between the “on” and “off” states can damage the materials and components in the ReRAM cell, thus affecting the memory element's lifetime and reliability.

Next, after delivering the “reset” switching pulse 213 it is common to apply a “sensing” pulse 212 to assure that the logic “zero” state has been achieved. Sensing pulse 212 is generally performed by applying a V_(READ) voltage (e.g., +0.5V) across the cell. If a “reset” operation was performed correctly, the current through the cell during this sensing step will equal the I_(OFF) current, which for the ReRAM cell will equal to the V_(READ) voltage divided by the sum of the current steering element resistance (R_(CSD)) and the resistance of the resistance switching layer.

FIG. 4 is a schematic side cross-sectional view of a ReRAM cell 400, in accordance with some embodiments. ReRAM cell 400 includes substrate 401 with various layers formed over it, such as electrode layers 102 and 104, current steering element 408, current limiting layer 402, and resistive switching layer 404. In some embodiments, ReRAM cell 400 also includes an intermediate electrode layer 406 to form a specifically configured interface with resistive switching layer 404.

Current limiting layer 402 is configured to limit the current passing through the layers of ReRAM cell and improve the overall switching performance and lifetime. Current limiting layer 402 is disposed within ReRAM cell 400 close to resistive switching layer 404 and/or current steering element 408 to effectively limit and/or prevent propagation of the programming current pulses (e.g., “set” or “reset” pulses) through ReRAM cell 400. This close proximity of current limiting layer 402 and resistive switching layer 404 and/or current steering element 408 is particularly useful in ReRAM cells 400 that utilize high speed transient programming pulses, such as square or trapezoidal shaped pulses that are less than about 1 microseconds in length. It is believed that the use of an externally positioned current limiting element (e.g., current limiters that are not embedded into ReRAM cells) will not effectively prevent the delivered high speed programming pulse energy from causing damage to the materials in resistive switching layer 404 and/or current steering element 408. Resistive switching layer 404 and/or current steering element 408 may break down when the high speed transient programming pulses are delivered through ReRAM cell 400, in particular when large currents are allowed to pulse through these components. It is believed that the propagation delay created during the transmission of the high speed programming pulse generally prevents the externally positioned current limiter from effectively reducing or dropping the instantaneous amount of energy passing through other components, such as resistive switching layer 404 and current steering element 408. In some embodiments, current limiting layer 402 is disposed in close proximity to resistive switching layer 404, such as directly interfacing resistive switching layer 404. One will note that the position of current limiting layer 402 in cell 400 need not be limited to the position shown in FIG. 4. Thus, the configuration as shown is not intended to be limiting as to the scope of the invention described herein. In some embodiments, current limiting layer 402 is disposed between resistive switching layer 404 and current steering element 408. Current limiting layer 402 can be disposed between intermediate electrode 406 and resistive switching layer 404 or between intermediate electrode 406 and current steering layer 408.

As described above, electrode layers 102 and 104 may be used to provide external connections to cell 400. In some embodiments, electrode layers 102 and 104 may each include more than one sub-layer of conductive material. For example, top electrode layer 102 may include a first electrode sub-layer 102 a and a second electrode sub-layer 102 b. Bottom electrode layer 104 may also include a first electrode sub-layer 104 a and a second electrode sub-layer 104 b. In this case, first electrode sub-layer 102 a and first electrode sub-layer 104 a (i.e., the external electrode sub-layers with respect to resistive switching layer 404) can be used to interconnect multiple ReRAM cells in the array, and thus may act as word-lines or bit-lines. Second electrode sub-layers 102 b and 104 b (i.e., the internal electrode sub-layers with respect to resistive switching layer 404) may each include a material that has desirable electrical properties (e.g., work function) so that these layers 102 b and 104 b can ensure resistive switching characteristics of ReRAM cell 400. First (external) electrode sub-layers 102 a and/or 104 a may be formed from tungsten (W), aluminum (Al) or copper (Cu). Second (internal) electrode sub-layers 102 b and/or 104 b may be formed from titanium (Ti), titanium nitride (TiN), or doped poly-silicon. One will note that the configuration shown in FIG. 4 and discussed herein is not intended to be limiting as to the scope of the invention described herein, since, for example, each of electrode layers 102 and 104 may include only conductive layer of the same composition. Overall, the position of the various layers, or number of layers, in the stack of layers used to form ReRAM cell may be altered without deviating from the basic scope of the invention described herein.

In some embodiments, current limiting layer 402 and second electrode sub-layer 102 b are formed as a single layer (not shown) that has suitable resistive and work function properties to ensure performance and usable life of ReRAM cell 400. Some examples of materials suitable for such multifunctional layers include hafnium nitride (Hf_(X)N_(X)).

FIG. 5 schematically illustrates an electrical circuit 50 formed by ReRAM cell 400 shown in FIG. 4. As illustrated in FIG. 5, electrical circuit 500 includes a top electrode impedance (i.e., resistance R_(TEL)) created by top electrode layer 102 layer(s), a current limiting layer impedance (i.e., resistance R_(RL)) created by current limiting layer 402, a resistive switching layer impedance (i.e., resistance R_(VR)) created by resistive switching layer 404, an intermediate electrode impedance (i.e., resistance R_(IEL)) created by intermediate electrode 406 layer(s), a current steering element impedance (i.e., resistance R_(CSD)) created by current steering element 408 and a bottom electrode impedance (i.e., resistance R_(BEL)) created by the bottom electrode layer 104 layer(s).

Referring back to FIG. 3, in one example, a “set” switching pulse 211, or “set” pulse 203, is delivered through the ReRAM cell to create a low resistance state, or logic “one” state. In this configuration, a “set” voltage V_(SET) is applied across the electrode layers and, which creates a “set” current I₃ to flow through the ReRAM cell, due to the impedance of the components in the ReRAM cell. The pulse 211 when applied to some embodiments of the ReRAM cell will generally achieve a “set” current I₃ during the later stages of the “set” operation as the resistive switching layer changes from the HRS to the LRS. The “set” current I₃ will equal the V_(SET) voltage divided by the sum of the impedances in the ReRAM cell.

Therefore, since the impedances of the electrodes are generally small, due to the need to reduce the power loss in the device, and the impedance of the variable current limiting layer is desirably low to achieve a logic “one” state, the impedance of the current steering element and the current limiting layer will dominate the circuit and the impedance of the circuit in this state is effectively equal to the sum of the impedances of the current steering element and the current limiting layer (i.e., R_(RL)+R_(CSD)). Therefore, referring to FIG. 3, the magnitude of the “set” current I₃ created by a “set” pulse 203 will equal a current (I₃), which can be adjusted by the selection of a desired fixed impedance value of the current limiting layer. One will note that due to the presence of the added impedance (R_(RL)) of the current limiting layer, the actual impedance (R_(CSD)*) of the current steering element will generally be greater than the impedance of a current steering element disposed in a cell that does not have the current limiting layer. As such, the added voltage drop provided by current limiting layer will prevent the current steering element from being damaged by the application of the programming currents during normal operation. In a ReRAM cell without a current limiting layer, the current steering element may often be operated near its breakdown voltage to reliably cause the resistive switching layer to switch as described above. This is generally not the case in the cell with the current limiting layer having a sufficient resistance due to the added voltage drop provided by this layer. The current limiting layer reduces the voltage applied across current steering element and, thus, prevents the impedance of the current steering element from dropping.

The impedance of a ReRAM cell containing a current limiting layer has to be optimized in order to reduce the power loss. FIG. 6 is a graph illustrating a plot of power loss (P) versus the magnitude of the current limiting layer impedance (R_(RL)) represented by trace 601. This power loss is created by passing a current through the current limiting layer. One will note that the power loss through the current limiting layer is equal to the square of the current (I) times the current limiting layer impedance (R_(RL)), or P=I²R_(RL). The current (I) through the ReRAM cell is equal to the applied voltage (V) across the electrode layers divided by the sum of the impedances in the circuit: I=V/(R_(TEL)+R_(RL)+R_(VR)+R_(IEL)+R_(CSD)+R_(BEL)). However, if it is assumed that resistive switching layer 404 is in its low resistance state and that the electrode impedances (e.g., R_(TEL), R_(IEL), R_(BEL)) are negligible as compared to the impedance of the current steering element impedance (R_(CSD)) and the current limiting layer (R_(RL)), the power loss (P) through the current limiting layer can be expressed as follows. P=I ² R _(RL)=(V ²/(R _(RL) +R _(CSD))²)R _(RL) =V ²/((R _(CSD) ² /R _(RL))+R _(RL)+2R _(CSD)) One will note that the power loss has an inflection point at which the power loss and current are a minimum. This point represents the case in which the current limiting layer's resistance is equal to current steering element's impedance (e.g., R_(RL)=R_(CSD)). Therefore, it may be desirable to form the current limiting layer, such that the magnitude of its impedance is substantially equal to the magnitude of the impedance of the current steering element impedance. One will note that in a more general case where the resistive switching layer impedance is not negligible relative to the current steering element impedance and the current limiting layer impedance, the inflection point will occur where the current limiting layer impedance is equal to the current steering element impedance plus resistive switching layer impedance at the LRS.

In order to improve switching characteristics of the resistive switching layer, a resistance of the current limiting layer is adjusted such that that the applied voltage (i.e., V_(SET) or V_(RESET)) generates the current within the following range: between the maximum allowable current, or load current I_(L), and the minimum current required to switch the device from one logic state to another (i.e., I_(MSC) or I_(MRC)). In some embodiments, the current limiting layer impedance R_(RL) is formed so that it has an impedance equal to a minimum “set” resistance (R_(MSR)) value, where the minimum “set” resistance (R_(MSR)) is equal to the minimum “set” voltage V_(MSET) applied across the electrode layers divided by the minimum “set” current (I_(MSC)) flowing through the device minus the sum of all of the other series resistance in the cell, or R _(MSR) =R _(RL)=[(V _(MSET)/(I _(MSC)))−(R _(TEL) +R _(VR) +R _(IEL) +R _(CSD) +R _(BEL))], where the minimum “set” voltage V_(MSET) is the “set” voltage required to achieve the minimum “set” current (I_(MSC)) through the cell. Therefore, assuming the resistive switching layer resistance and the electrode resistances are much smaller than the current steering element impedance (R_(CSD)) when the resistive switching layer is in the low resistance state the minimum “set” resistance will approximately equal the following: R _(MSR) =R _(RL)=(V _(MSET)/(I _(MSC)))−R _(CSD).

In general, it is desirable to assure that the current limiting layer impedance R_(RL) is non-zero to prevent the current flowing through the cell from reaching the load current (IL). In one example, it is desirable to form the current limiting layer that has a resistance equal to an impedance that is between about 75% and about 125% of the impedance of the current steering element impedance (R_(CSD)). In one example, the current limiting layer impedance (R_(RL)) is between about 10 kΩ and about 10 MΩ, such as between about 100 kΩ and about 1 MΩ.

As the size of ReRAM cells shrink to improve device performance and storage capacity, the programming parameters that cause resistive switching layer 404 to switch also need to be adjusted. Typically, the programming parameters that need to be adjusted as device size is reduced include the applied switching current (I_(switch)) and voltage drop applied across the resistive switching layer. In general, a device's programming parameters are limited by the maximum applied voltage (V_(MAV)), which is usually defined for each type of device by industry standards and/or by a device manufacturer's device “product specification.” In one example, the product specification for a 65 nm technology node non-volatile memory device has a maximum applied voltage (V_(MAV)) of about 8 Volts. To reliably cause a ReRAM cell to switch, it is believed that both the voltage drop applied across the resistive switching layer needs to be above a minimum switching voltage (V_(MSV)) and the current delivered through the resistive switching layer must be greater than the minimum switching current (I_(MSWC)). It is believed that the electric field created in resistive switching layer 404, due to the application of a voltage greater than the minimum switching voltage (V_(MSV)), and the application of a current greater than the minimum switching current (I_(MSWC)) will cause the movement and alignment in LRS or non-alignment in HRS, of the vacancy type defects in the resistive switching layer, which causes the resistive switching layer to more reliably switch between the desirable LRS and HRS. It is also believed that the electric field created by the minimum switching voltage (V_(MSV)) and application of the minimum switching current (I_(MSWC)) are both required to assure that all of the devices in an array of formed ReRAM cells will all reliably switch. It is noted that by adjusting the material properties of the resistive switching layer (e.g., material composition, thickness, defect density, crystal structure) the switching characteristics of resistive switching layer 404 can be adjusted.

However, as noted above, the ability to provide a voltage drop across the resistive switching layer that exceeds the minimum switching voltage (V_(MSV)) and provide a current that exceeds the minimum switching current (I_(MSWC)) is limited by the maximum applied voltage (V_(MAV)). The voltage drops formed within the ReRAM cell when a maximum applied voltage (V_(MAV)) is applied, will equal the sum of the voltage drops across the cell, which can be defined as follows. V _(MAV) =ΣΔV _(i) ≈ΔV _(TEL) +ΔV _(RL) αΔV _(VR) +ΔV _(IEL) +ΔV _(CSD) +ΔV _(BEL) Stated another way, the maximum applied voltage (V_(MAV)) will cause an applied current (I_(MAV)) to flow through the total resistance (R_(Total)) of the cell. V _(MAV) =I _(MAV) ×R _(Total) =I _(MAV) ×ΣR _(i); or V _(MAV) ≈I _(MAV)×(R _(TEL) +R _(RL) +R _(VR) +R _(IEL) +R _(CSD) +R _(BEL)) If it is assumed that the electrode impedances (e.g., R_(TEL), R_(IEL), R_(BEL)) are negligible, as compared to the current limiting layer impedance (R_(RL)), the current steering element impedance (R_(CSD)) and the resistive switching layer impedance (R_(VR)) the equation (s) can be further simplified to the following: V _(MAV) ≈I _(MAV)×(R _(RL) +R _(VR) +R _(CSD))=ΔV _(RL) +ΔV _(VR) +ΔV _(CSD) Therefore, if one assumes that the resistance of resistive switching layer 404 in either the high or the low resistance states remains relatively constant during the useable life of the device, and that the current limiting layer impedance is as large as possible (i.e., maximum resistance layer impedance (R_(RL)*)), while still allowing the device to reliably switch, the generated applied current (I_(MAV)) will equal the minimum switching current (I_(MSWC)) and the load resistance will equal the following: R _(RL)*=(V _(MAV) /I _(MSWC))−(R _(VR) +R _(CSD))  (1)

Where R_(VR) is either in a high resistance state or in a low resistance state depending on whether the device is in LRS or HRS, the minimum switching current (I_(MSWC)) will vary depending on the type of operation being performed (e.g., switching between LRS and HRS) and the R_(CSD) varies depending whether it is forward or reverse biased. If the resistance layer impedance (R_(RL)) exceeds the maximum resistance layer impedance (R_(RL)*) the device will not reliably switch between operating states, and thus should be avoided.

In some embodiments, a ReRAM cell used for 65 nm technology node has a maximum applied voltage (V_(MAV)) of about 8 Volts. The maximum resistance of the current limiting layer (R_(RL)*) may be less than about 590-600 kilo-Ohms, so that a minimum switching current of about 10 micro-Amperes can be generated during a “reset” operation. In the same type of device, the minimum switching current of about 610 nano-Amperes can be achieved during a “set” operation. One will note that in these examples, the resistive switching layer impedance (R_(VR)) in the LRS state may be about 200 kilo-Ohms, while its impedance in the HRS state may be about 2.5 mega-Ohms. In the same example, the current steering element impedance (R_(CSD)) in the forward direction may be about 10 kilo-Ohms and in the reverse direction may be about 10 mega-Ohms.

Referring to FIG. 3, in general, it is desirable to form current limiting layer 402 so that its impedance (R_(RL)) limits the current through a ReRAM cell to a value (e.g., current I₂) that is just greater the minimum “set” current I_(MSC), as illustrated by pulse 402, and still allow the “on” logic state to be reliably “set” by the applied V_(SET) voltage. It is believed that by adding current limiting layer 402 to a ReRAM cell can also help reduce the apparent minimum I_(MSC) current required to cause resistive switching layer 404 to change to a low resistive state, since the addition of the current limiting layer impedance (R_(RL)) in the circuit will reduce the swing in current between the “set” and “reset” switching currents at the same fixed applied voltage, thus affecting the density and movement of the traps in the resistive switching layer. Not intending to be bound by theory, it is believed that when a smaller switch current is applied to a device, the formed filament(s) or aligned traps will be smaller in size than if a higher switching current is applied, thus making the filament(s) easier to alter during the “reset” phase of the resistive switching process.

In some embodiments, a resistance of the current limiting layer (R_(RL)) is greater than the resistance of the current steering element (R_(CSD)). These configurations may prevent the “set” programming current from reaching the load current (I_(L)) when the maximum applied voltage (V_(MAV)) is applied. Furthermore, these configurations may allow the ReRAM cell to reliably switch during the “set” operation and/or to minimize the magnitude of the peak “reset” programming current (e.g., current I_(C)).

It should be noted that the minimum switching voltage V_(MSV) and/or minimum switching current (I_(MSWC)) depend on whether the ReRAM cell is in LRS or HRS. The minimum switching voltage can be written as the following. V _(MSV) =V _(MAV)−(I _(MSWC)×(R _(RL) +R _(CSD))) Since the switching characteristics of resistive switching layer 404 depend on its electrical and physical properties, tuning of the current limiter's resistance (R_(RL)) is important, since it effectively limits the switching characteristics of resistive switching layers 404. Therefore, the current limiter's resistance (R_(RL)) may drive the type of resistive switching materials and/or switching layer properties that can be used in a reliable device.

In some embodiments, the current limiting layer is formed from a material that will not significantly vary in resistance when the “set” and “reset” switching voltages are applied to the cell. Forming the current limiting layer from a material that has a generally constant resistance assures that the switching characteristics of the ReRAM cell do not change over the life of the cell. Also, forming the current limiting layer from a material that does not significantly vary in resistance during the programming steps provide less variability in the electrical properties of the formed layer due to variations in the deposition process (e.g., defect density variations). It also provides less variability in the electrical properties of the formed layer over the lifetime of the ReRAM cell due to any physical or chemical change in the current limiting layer material. Furthermore, it allows a lower device performance variability that is created by differences in the “forming” process (i.e., application of the forming voltage (V_(FORM))). In some embodiments, the current limiting layer has a single resistive state, since it does not significantly vary in resistance during the electrical “forming” and/or programming steps. The material and electrical properties of the current limiting layer do not degrade or breakdown during the electrical “forming” process, and also during normal repetitive operation of the ReRAM cell.

Device Structure and Formation Processes

As illustrated in FIG. 4 and briefly described above, ReRAM cell 400 may include a first electrode layer 102, a current limiting layer 402, a resistive switching layer 404, an intermediate electrode layer 406, a current steering element 408 and a second electrode layer 104. In some embodiments, current steering element 408 includes a p-n junction diode, p-i-n diode, transistor, or other similar device that is disposed between electrode layer 102 and resistive switching layer 404 or between electrode layer 104 and resistive switching layer 404. Current steering element 408 may include two or more layers of a semiconductor material, such as two or more doped silicon layers, that are configured to direct the flow of current through the device. In one example, the current steering element is a diode that includes a p-doped silicon layer (not shown), an un-doped intrinsic layer (not shown), and an n-doped silicon layer (not shown) that has an overall resistance between about 1 kilo-Ohm and about 100 mega-Ohms. The overall resistance will generally depend on the type of current steering element that is formed and in what direction current is flowing through the device (e.g., forward or reversed biased).

Electrode layers 102, 406, and 104 disposed in ReRAM cell 400 are generally formed from a conductive material that has a desirable conductivity and work function. In some configurations, each of electrode layers 102, 406, and/or 104 is formed from different materials, which may include, but are not limited to p-type polysilicon, n-type polysilicon, transition metals, transition metal alloys, transition metal nitrides, and transition metal carbides. In some embodiments, electrode layers 102 and/or 104 include a metal, metal alloy, metal nitride or metal carbide formed from one or more of titanium (Ti), tungsten (W), tantalum (Ta), cobalt (Co), molybdenum (Mo), nickel (Ni), vanadium (V), hafnium (Hf) aluminum (Al), copper (Cu), platinum (Pt), palladium (Pd), iridium (Ir), ruthenium (Ru), and combination thereof. In some embodiments, electrode layers 102 and/or 104 include a metal alloy, such as a titanium/aluminum alloy or a silicon-doped aluminum (AlSi). Electrode layers 102 and 104 may include a metal, such as a transition metal, transition metal alloy, transition metal carbide, transition metal nitride (e.g., TiN). Intermediate electrode layer 406 may include a heavily doped semiconductor material, such as a heavily doped silicon material (e.g., n-type polysilicon material) that interfaces well with current steering element 408. In one example, intermediate electrode layer 406 includes polysilicon. The thickness of intermediate electrode layer 406 may be between about 50 and about 500 Angstroms, while the thickness of electrode layers 102 and 104 may be between about 50 and 5000 Angstroms each.

Resistive switching layer 404 may be formed from a dielectric material, such as a metal oxide material or other similar material. This material can be switched between at least two or more stable resistive states. In some embodiments, resistive switching layer 404 is a high bandgap material (e.g., bandgap >4 electron volts (eVs)), such as hafnium oxide (Hf_(x)O_(y)), tantalum oxide (Ta_(x)O_(y)), aluminum oxide (Al_(x)O_(y)), lanthanum oxide (La_(x)O_(y)), yttrium oxide (Y_(x)O_(y)), dysprosium oxide (Dy_(x)O_(y)), ytterbium oxide (Yb_(x)O_(y)) and zirconium oxide (Zr_(x)O_(y)). It has been found that using high band gap resistive switching layer materials may improve data retention in a ReRAM cell, and reduce the leakage current in the formed memory element device, since the amount of trapped charge in the resistive switching layer material will be less than a lower band gap material, and the high band gap materials create a large barrier height that the carriers have to cross during the read, “set” and “reset” operations. In other embodiments, lower bandgap metal oxide materials can be used, such as titanium oxide (TiO_(x)), nickel oxide (NiO_(x)) or cerium oxide (CeO_(x)) may be advantageous for some embodiments. In some cases, a semiconductive metal oxide (p-type or n-type) such as zinc oxides (Zn_(x)O_(y)), copper oxides (Cu_(x)O_(y)), and their nonstoichiometric and doped variants can be used. Resistive switching layer 404 may have a thickness of between about 10 and about 100 Angstroms. In some embodiments, resistive switching layer 404 is doped with a material that has an affinity for oxygen (e.g., transition metals (Al, Ti, Zr)) to form a metal-rich resistive switching layer (e.g., HfO_(1.7) vs. HfO₂), which is deficient in oxygen, and thus has a larger number of oxygen vacancy type defects. The additional vacancy defects can reduce the required switching and forming voltages, reduce the device operating current(s), and reduce the device to device variation in a formed memory element. In some embodiments, resistive switching layer 404 includes a metal oxide layer, such as Hf_(x)O_(y), Ta_(x)O_(y), Al_(x)O_(y), La_(x)O_(y), Y_(x)O_(y), Dy_(x)O_(y), Yb_(x)O_(y) and/or Zr_(x)O_(y), formed to a thickness of between about 20 and about 100 Angstroms, such as between about 30 and about 50 Angstroms. Resistive switching layer 404 can be deposited using any desired technique, but in some embodiments described herein is deposited using an atomic layer deposition (ALD) process. In other embodiments, resistive switching layer 404 can be deposited using a chemical vapor deposition (CVD) (e.g., low pressure CVD, plasma enhanced CVD) or ALD (e.g., plasma enhanced ALD), physical vapor deposition (PVD), liquid deposition processes, and epitaxy processes. It is believed that PEALD processes can be used to control defects and improve switching and forming voltages in some embodiments. In one example, an ALD process using tetrakis(dimethylamino)hafnium (TDMAH) and an oxygen containing precursor at a temperature of about 250° C. is used to form an 50 Angstroms thick hafnium oxide (Hf_(x)O_(y)) containing resistive switching layer 404.

Current limiting layer 402 is formed from a suitable material that can be reliably and consistently formed and operated within ReRAM cell 500 as described elsewhere in this document. In some embodiments, a material of current limiting layer 402 has a suitable work function for controlling the electron flow between current limiting layer 402 and resistive switching layer 404. This selection may alter the magnitude of the generated I_(ON) and I_(OFF). In some embodiments, current limiting layer 402 is used to increase or decrease the formed barrier height at the interface with resistive switching layer 404. This feature is used to improve current flowing characteristics and reduce the magnitude of the I_(ON) and I_(OFF) currents. It should be noted that these changes in the barrier height will generally not affect the current ratio (I_(ON)/I_(OFF)), and thus not impacts detectability of different resistive states.

To achieve a current limiting layer that has desirable electrical and/or physical properties, its composition and/or deposition conditions may be specifically controlled. As discussed above, the resistance of current limiting layer 402 may be matched to the resistance of current steering element 408. In additional to the resistive properties of the material forming current limiting layer 402, the structural aspects of current limiting layer 402 may be controlled. Specifically, the resistance (R) is equal to the resistivity (ρ) of the material forming a structure times the length (L) of the structure divided by its cross-sectional area (A) of the structure (i.e., R=ρ(L/A)). The cross-sectional area (A) is generally fixed by the size and lateral spacing of ReRAM cells, and thus cannot be easily varied. As such, the resistance control is generally achieved by adjusting the thickness of the current limiting layer and/or the resistivity (ρ) of the material used to form the layer. In some embodiments, a ReRAM cell that is about 150 nm×150 nm is size has a current limiting layer that is about 300 Angstroms thick and is formed from materials that has a resistivity of 75 Ohm-cm. As such, this current limiting layer has a resistance of about 1 mega-Ohm. In some embodiments, the current limiting layer is formed such that its resistance (R_(RL)) is between about 10 kilo-Ohm and about 10 mega-Ohm, such as between about 100 kilo-Ohm and about 1 mega-Ohm.

Resistivity (ρ) is an intrinsic property of the material and can be controlled by adjusting the composition of the material. Some examples, include adding alloying elements or doping atoms and/or adjusting the morphological structure of the materials, (e.g., shifting from amorphous to crystal structure). In some embodiments, a current limiting layer may include titanium oxide doped with niobium, tin oxide doped with antimony, or zinc oxide doped with aluminum. In general, a current limiting layer may include a binary or multiphase compound. Some examples include HfN, HfSi, HfSiN, HfSiON, TaN, TiSi, TaSiN, TaSiON, TiSi, TiSiN, TiSiON, SiN, and SiON. In some embodiments, the material forming the current limiting layer has an amorphous structure. The concentration of dopant materials in the base material may be between about 0.5 atomic percent and 25 atomic percent or, more specifically, between about 1 atomic percent and 10 atomic percent. Dopant concentrations could be varied to achieve suitable resistivity levels of the material forming the current limiter. For example, a current limiter material may have resistivity of at least about 1 Ohm-cm or, more specifically, at least about 10 Ohm-cm, or even more specifically, 100 Ohm-cm. The resistivity of the current limiting layer may remain substantially unchanged upon applying substantial electrical fields to the layer. In some embodiments, the resistivity of the current limiting layer changes by less than 10% upon applying an electrical field of 1 MV/cm.

In some embodiments, current limiting layer 402 includes a semiconductor and/or dielectric material that has a breakdown voltage greater than the breakdown voltage of the materials forming resistive switching layer 404. The lower breakdown voltage may cause various forms of damage the ReRAM cell as discussed above. In some embodiments, the breakdown voltage of the materials forming current limiting layer 402 is at least about 8 V or, more specifically, at least about 10V.

The thickness of current limiting layer 402 may be less than about 200 Angstroms or, more specifically, less than about 100 Angstroms or even less than 50 Angstroms. The lower thickness may be desirable from a scaling perspective but properties of the materials may be difficult to control at the necessary level for such thin layer. Such thin current limiting layer may be formed using various deposition techniques, such as physical vapor deposition (PVD), atomic layer deposition (ALD), and chemical vapor deposition (CVD) as further described below.

ReRAM Cell Fabrication Processes

FIG. 7 illustrates a process sequence 700 that can be used to form a ReRAM cell, in accordance with some embodiments. Sequence 700 may start with operation 702, during which a first electrode layer is formed. The first electrode layer may be bottom electrode layer 104 or intermediate electrode 406, both shown in FIG. 4. Operation 702 may also involve forming current steering element 408. One or more of these components of a ReRAM cell may be formed over a substrate 501, such as a silicon substrate. Physical vapor deposition (PVD), chemical vapor deposition (CVD), atomic layer deposition (ALD), or other similar techniques may be used for these purposes. In some embodiments, the empirical or theoretical resistance of current steering element 408 is determined based on its materials and methods of fabrication. This information is used to design current limiting layer 402 with a specific resistance that would correlate to the resistance of current steering element 408 as described above. In some embodiments, current steering element 408 is a diode that includes a p-doped silicon layer, an un-doped intrinsic layer, and an n-doped silicon layer. All three layers may be formed by CVD techniques. In some embodiments, electrode 104 includes a titanium nitride layer that is between about 50 and 1,000 nanometers thick and is formed using a PVD technique.

Intermediate electrode layer 406 including highly doped polysilicon may be formed is CVD or ALD techniques. In some embodiments, an optional native oxide layer removal operation may be performed after forming intermediate electrode layer 406. For example, a wet chemical processing technique or a dry clean process may be performed.

Sequence 700 may proceed with forming a resistive switching layer during operation 704. The resistive switching layer may be deposited over the intermediate electrode layer, if one is present, or over the bottom electrode layer. The resistive switching layer may be deposited using a PVD, CVD or ALD technique. The deposited resistive switching layer may include a metal oxide layer, such as Hf_(x)O_(y), Ta_(x)O_(y), Al_(x)O_(y), La_(x)O_(y), Y_(x)O_(y), Dy_(x)O_(y), Yb_(x)O_(y) and/or Zr_(x)O_(y). The thickness of this layer may between about 20 and 100 Angstroms, such as between about 30 and 50 Angstroms. In some embodiments, the resistive switching layer is deposited using an ALD technique. Tetrakis(dimethylamino)hafnium (TDMAH) may be used as a precursor that is oxidized into hafnium oxide using an oxygen containing reagent (e.g., water vapor). The processing temperature may be about 250° C.

Sequence 700 may proceed with depositing a current limiting layer over the resistive switching layer or some other layer during operation 706. Various examples and variations of the stack structure are described above with reference to FIG. 4. PVD, CVD, or ALD or other similar techniques may be used for depositing a current limiting layer. In some embodiments, the current limiting layer includes a metal oxide and a dopant. The current limiting layer may be formed to a thickness between about 50 and about 500 Angstroms. In some embodiments, the current limiting layer including titanium oxide doped with niobium may be deposited reactive sputtering. A titanium metal target may be bombarded in the oxygen containing environment.

In some embodiments, titanium and niobium targets may be bombarded with argon ions in oxygen environment to deposit a layer that include both titanium oxide and niobium oxide. These oxides may be deposited either simultaneously or sequentially. The base material and dopant compositions are tailored by controlling the respective deposition times, atmospheres, pressures, and powers. For example, low doping levels may be achieved by using long base material deposition time followed by short dopant deposition time.

Sequence 700 may proceed with forming another electrode during operation 708. This second electrode may be formed over the current limiting layer, resistive switching layer, or some other layer depending on the configuration of the stack described above with reference to FIG. 4. Deposition of the second electrode may be performed using a process similar to the deposition of the first electrode described above with reference to operation 702.

During optional operation 710, ReRAM stack may be optionally annealed. Annealing may be performed at a temperature of at least about 550° C. or, more specifically, at a temperature of at least about 700° C. For example, the stack may be heated to between about 550° C. and 1000° C. for between about 30 seconds and 20 minutes Annealing operation 710 may be specifically tuned to form various interfaces between adjacent layers in the stack, such as between the current limiting layer and its adjacent layer Annealing operation 710 may be also used to activate and/or further process other layers formed in the ReRAM cell.

In some embodiments, the current limiting layer is formed as part of or after formation of the second electrode during operation 708 by, for example, adjusting one or more process gas flows used in the CVD or ALD. As a result, two different layers may be formed in the same operation. Specifically, a current limiting layer may be formed at the beginning or at the end of electrode layer deposition process by reducing the amount or flow of a dopant precursor gas in the chamber to form less doped layer that has a higher resistivity.

ReRAM Cell Examples

Various examples of ReRAM cells will now be presented. In some embodiments, a ReRAM cell includes a intermediate electrode containing an n-doped polysilicon layer, a resistive switching layer that is between about 30-100 Angstroms thick and that contains hafnium oxide, a current limiting layer that is between about 50 and 500 Angstroms thick and includes titanium oxide doped with niobium, and a second electrode that includes titanium nitride. The niobium dopant concentration in the titanium oxide may be between 0.5 and 25 atomic % or, more specifically, between 1 and 10 atomic %.

In one example, a ReRAM cell includes a intermediate electrode containing an n-doped polysilicon layer, a resistive switching layer that is between about 30-100 Angstroms thick and that contains hafnium oxide, a current limiting layer that is between about 50 and 500 Angstroms thick and includes tin oxide doped with antimony, and a second electrode that includes titanium nitride. The antimony dopant concentration in the tin oxide may be between 0.5 and 25 atomic % or, more specifically, between 1 and 10 atomic %.

In yet another example, a ReRAM cell includes a first electrode intermediate electrode containing an n-doped polysilicon layer, a resistive switching layer that is between about 30-100 Angstroms thick and that contains hafnium oxide, a current limiting layer that is between about 50 and 500 Angstroms thick and includes zinc oxide doped with aluminum, and a second electrode that includes titanium nitride. The aluminum dopant concentration in the zinc may be between 0.5 and 25 atomic % or, more specifically, between 1 and 10 atomic %.

The foregoing is merely illustrative of the principles of this invention and various modifications can be made by those skilled in the art without departing from the scope and spirit of the invention as defined by the claims that follow. The dopant concentration may be 0.5 and 25 atomic % or, more specifically, between 1 and 10 atomic %. 

What is claimed is:
 1. A resistive random access memory cell comprising: a first electrode layer; a second electrode layer; a third layer operable as a current limiter, the third layer comprising one of tin oxide doped with antimony or zinc oxide doped with aluminum, the third layer disposed between the first electrode layer and the second electrode layer; and a fourth layer operable as a resistive switching layer and comprising a resistive switching material, the fourth layer disposed between the first electrode layer and the second electrode layer, a current steering element, wherein the fourth layer is disposed between the current steering element and the third layer, wherein a breakdown voltage of the third layer is greater than a breakdown voltage of the fourth layer, and wherein a resistance of the third layer is between about 75% and about 125% of a resistance of the current steering element.
 2. The resistive random access memory cell of claim 1, wherein the third layer comprises tin oxide doped with antimony.
 3. The resistive random access memory cell of claim 1, wherein the third layer comprises zinc oxide doped with aluminum.
 4. The resistive random access memory cell of claim 1, wherein a concentration of antimony in the third layer comprising tin oxide doped with antimony or a concentration of aluminum in the third layer comprising zinc oxide doped with aluminum is between 0.5 atomic percent and 25 atomic percent.
 5. The resistive random access memory cell of claim 1, wherein a concentration of antimony in the third layer comprising tin oxide doped with antimony or a concentration of aluminum in the third layer comprising zinc oxide doped with aluminum is between 1 atomic percent and 10 atomic percent.
 6. The resistive random access memory cell of claim 1, wherein the third layer has a resistivity of at least 5 Ohm-cm controlled by a concentration of antimony in the third layer comprising tin oxide doped with antimony or a concentration of aluminum in the third layer comprising zinc oxide doped with aluminum.
 7. The resistive random access memory cell of claim 1, wherein the third layer has a resistivity of at least 10 Ohm-cm controlled by a concentration of antimony in the third layer comprising tin oxide doped with antimony or a concentration of aluminum in the third layer comprising zinc oxide doped with aluminum.
 8. The resistive random access memory cell of claim 1, wherein the third layer has a thickness of less than 200 Angstroms to control the resistance of the third layer.
 9. The resistive random access memory cell of claim 1, wherein the third layer has a thickness of less than 100 Angstroms to control the resistance of the third layer.
 10. The resistive random access memory cell of claim 1, wherein the third layer has a thickness of less than 50 Angstroms to control the resistance of the third layer.
 11. The resistive random access memory cell of claim 1, wherein a resistivity of the third layer is configured to change by less than 10% in response to the application of an electrical field of 1 MV/cm.
 12. The resistive random access memory cell of claim 1, wherein the third layer has an amorphous structure.
 13. The resistive random access memory cell of claim 1, wherein the resistive switching material comprises one of hafnium oxide, aluminum oxide, tantalum oxide, zirconium oxide, or yttrium oxide.
 14. The resistive random access memory cell of claim 1, wherein the first electrode layer comprises one of silicon, titanium, titanium nitride, platinum, iridium, iridium oxide, ruthenium, or ruthenium oxide.
 15. The resistive random access memory cell of claim 1, wherein the resistive switching material of the fourth layer comprises a metal-rich metal oxide.
 16. The resistive random access memory cell of claim 1, wherein the resistance of the third layer is substantially the same as the resistance of the current steering.
 17. A resistive random access memory cell comprising: a first electrode layer comprising n-doped polysilicon; a second electrode layer comprising titanium nitride; a third layer operable as a current limiter, the third layer comprising one of tin oxide doped with antimony or zinc oxide doped with aluminum, wherein a concentration of antimony in the third layer comprising tin oxide doped with antimony or a concentration of aluminum in the third layer comprising zinc oxide doped with aluminum is between 1 atomic percent and 10 atomic percent, the third layer disposed between the first electrode layer and the second electrode layer and having a thickness of less than 100 Angstroms; and a fourth layer operable as a resistive switching layer and comprising hafnium oxide, the fourth layer disposed between the first electrode layer and the second electrode layer, a current steering element, wherein the fourth layer is disposed between the current steering element and the third layer, wherein a breakdown voltage of the third layer is greater than a breakdown voltage of the fourth layer, and wherein a resistance of the third layer is between about 75% and about 125% of a resistance of the current steering element.
 18. A method of forming a resistive random access memory cell, the method comprising: forming a first electrode layer over a substrate; forming a third layer operable as a current limiter, the third layer comprising one of tin oxide doped with antimony or zinc oxide doped with aluminum; and forming a fourth layer operable as a resistive switching layer and comprising a resistive switching material; and forming a current steering element, forming a second electrode layer, wherein a breakdown voltage of the third layer is greater than a breakdown voltage of the fourth layer, and wherein a resistance of the third layer is between about 75% and about 125% of a resistance of the current steering element.
 19. The method of claim 18, wherein the third layer is formed using one of a reactive sputtering technique, a co-sputtering technique, or an atomic layer deposition technique.
 20. The method of claim 18, wherein forming the third layer comprises transferring the dopant from the fourth layer and into the third layer by annealing. 